作者： 时间：2018-08-28
本文总结了在185nm~3500nm范围内的折射率参数，方便用户查询石英在不同波长的折射率，石英折射率，熔融石英折射率。
|
入射光波长λ（nm） |
水晶熔制石英玻璃折射率 |
合成石英玻璃折射率 |
|
185.41 |
1.57464 |
- |
|
193.53 |
1.56071 |
- |
|
202.54 |
1.54729 |
1.54717 |
|
206.20 |
1.54269 |
1.54266 |
|
213.85 |
- |
1.53434 |
|
214.45 |
1.53385 |
- |
|
226.50 |
1.52318 |
1.52299 |
|
232.94 |
1.51834 |
- |
|
237.83 |
- |
1.51473 |
|
248.20 |
- |
1.50841 |
|
250.20 |
1.50762 |
- |
|
257.62 |
1.50397 |
1.50351 |
|
265.36 |
- |
1.49994 |
|
274.87 |
1.49634 |
- |
|
280.35 |
- |
1.49403 |
|
289.36 |
- |
1.49098 |
|
298.06 |
1.48859 |
1.48837 |
|
307.59 |
- |
1.48575 |
|
313.17 |
- |
1.48433 |
|
328.36 |
1.48183 |
- |
|
334.15 |
- |
1.47976 |
|
340.36 |
1.47877 |
1.47860 |
|
346.69 |
1.47766 |
1.47748 |
|
361.17 |
1.47513 |
1.47503 |
|
365.48 |
- |
1.47448 |
|
398.84 |
1.47028 |
- |
|
404.65 |
- |
1.46961 |
|
435.83 |
1.46679 |
1.46669 |
|
486.13 |
1.46324 |
1.46314 |
|
546.07 |
1.46021 |
1.46007 |
|
587.56 |
1.45857 |
1.45847 |
|
656.27 |
1.45646 |
1.45637 |
|
670.00 |
1.456066 |
- |
|
680.00 |
1.455818 |
- |
|
690.00 |
1.455579 |
- |
|
700.00 |
1.455347 |
- |
|
800.00 |
1.453371 |
- |
|
900.00 |
1.451808 |
- |
|
1000.00 |
1.450473 |
- |
|
1100.00 |
1.440261 |
- |
|
1200.00 |
1.448110 |
- |
|
1300.00 |
1.446980 |
- |
|
1400.00 |
1.445845 |
- |
|
1500.00 |
1.444687 |
- |
|
1600.00 |
1.443492 |
- |
|
1700.00 |
1.442250 |
- |
|
1800.00 |
1.440954 |
- |
|
1900.00 |
1.439957 |
- |
|
2000.00 |
1.438174 |
- |
|
2100.00 |
1.436680 |
- |
|
2200.00 |
1.435111 |
- |
|
2300.00 |
1.433462 |
- |
|
2400.00 |
1.431730 |
- |
|
2500.00 |
1.429911 |
- |
|
2600.00 |
1.428001 |
- |
|
2700.00 |
1.425995 |
- |
|
2800.00 |
1.423891 |
- |
|
2900.00 |
1.421684 |
- |
|
3000.00 |
1.419370 |
- |
|
3100.00 |
1.416940 |
- |
|
3200.00 |
1.414400 |
- |
|
3300.00 |
1.411730 |
- |
|
3400.00 |
1.408930 |
- |
|
3500.00 |
1.406010 |
- |
|
注：测量误差：±3x10-5 |
||
实际工程制造使用中，熔融石英有一些常用的品牌和型号，例如国产熔融石英、光学石英玻璃常用的标号有JGS1、JGS2、JGS3，它们的折射率完全一致。进口的熔融石英玻璃品牌型号有康宁7980；OHARA的SK-1300、S-TIH10、SK-1310、S-TIH53W；肖特BF33、BK7以及Heraeu的Suprasil 3001/3002/300、Infrasil 301/302等。本文统计了JGS1、JGS2、JGS3、7980、SK-1300、S-TIH10、SK-1310、S-TIH53W 、BF33、BK7、Suprasil 3001/3002/300、Infrasil 301/302等光学熔融石英材料在不同波长下的折射率。
以下为JGS1、JGS2、JGS3、7980、SK-1300和BF33等石英玻璃材料在不同波长下的折射率
一、JGS1、JGS2、JGS3石英玻璃折射率表
|
波长（nm） |
折射率（n） |
波长（nm） |
折射率（n） |
|
200 |
1.55051 |
1000 |
1.45042 |
|
220 |
1.52845 |
1064 |
1.44962 |
|
250 |
1.50745 |
1100 |
1.44920 |
|
300 |
1.48779 |
1200 |
1.44805 |
|
320 |
1.48274 |
1300 |
1.44692 |
|
360 |
1.47529 |
1500 |
1.44462 |
|
400 |
1.47012 |
1600 |
1.44342 |
|
450 |
1.46557 |
1700 |
1.44217 |
|
488 |
1.46302 |
1800 |
1.44087 |
|
500 |
1.46233 |
1900 |
1.43951 |
|
550 |
1.46008 |
2000 |
1.43809 |
|
588 |
1.45860 |
2200 |
1.43501 |
|
600 |
1.45804 |
2400 |
1.43163 |
|
633 |
1.45702 |
2600 |
1.42789 |
|
650 |
1.45653 |
2800 |
1.42377 |
|
700 |
1.45529 |
3000 |
1.41925 |
|
750 |
1.45424 |
3200 |
1.41427 |
|
800 |
1.45332 |
3370 |
1.40990 |
|
850 |
1.45250 |
3507 |
1.40566 |
|
900 |
1.45175 |
3707 |
1.39936 |
二、美国康宁7980熔融石英玻璃折射率表
条件：22 ˚C, 760 mm Hg, N2
|
波长（nm） |
折射率（n） |
|
184.950 |
1.575017 |
|
194.227 |
1.558918 |
|
206.266 |
1.542665 |
|
214.506 |
1.533722 |
|
228.872 |
1.521154 |
|
253.728 |
1.505522 |
|
312.657 |
1.484493 |
|
334.244 |
1.479764 |
|
365.119 |
1.474539 |
|
404.770 |
1.469615 |
|
435.957 |
1.466691 |
|
486.269 |
1.463123 |
|
546.227 |
1.460076 |
|
587.725 |
1.458461 |
|
632.990 |
1.457016 |
|
656.454 |
1.456364 |
|
706.714 |
1.455144 |
|
852.344 |
1.452463 |
|
1014.260 |
1.450241 |
|
1128.950 |
1.448866 |
三、OHARA SK-1300熔融石英折射率表
|
波长（nm） |
20℃ |
25℃ |
折射率随温度变化的变化率1×10－6／℃ |
|
365.015 |
1.47459 |
1.47465 |
11.2 |
|
404.656 |
1.46967 |
1.46972 |
10.8 |
|
435.835 |
1.46675 |
1.46680 |
10.6 |
|
486.133 |
1.46318 |
1.46323 |
10.3 |
|
546.075 |
1.46013 |
1.46018 |
10.1 |
|
587.562 |
1.45852 |
1.45857 |
10.0 |
|
656.273 |
1.45642 |
1.45647 |
9.9 |
四、OHARA S-TIH10熔融石英折射率表
|
入射光波长λ（nm） |
折射率 |
|
2325.42 |
1.67934 |
|
1970.09 |
1.68562 |
|
1529.58 |
1.69286 |
|
1128.64 |
1.70040 |
|
1013.98 |
1.70330 |
|
852.11 |
1.70884 |
|
768.19 |
1.71292 |
|
706.52 |
1.71683 |
|
656.27 |
1.72086 |
|
643.85 |
1.72202 |
|
632.8 |
1.72310 |
|
589.29 |
1.72803 |
|
587.56 |
1.72825 |
|
546.07 |
1.73429 |
|
486.13 |
1.74645 |
|
479.99 |
1.74802 |
|
441.57 |
1.75987 |
|
435.835 |
1.76200 |
|
404.656 |
1.77595 |
五、OHARA SK-1310熔融石英折射率表
|
入射光波长λ（nm） |
折射率 |
|
2325.42 |
1.43320 |
|
1970.09 |
1.43876 |
|
1529.58 |
1.44449 |
|
1128.64 |
1.44908 |
|
1013.98 |
1.45045 |
|
852.11 |
1.45267 |
|
768.19 |
1.45409 |
|
706.52 |
1.45535 |
|
656.27 |
1.45657 |
|
643.85 |
1.45690 |
|
632.8 |
1.45722 |
|
589.29 |
1.45860 |
|
587.56 |
1.45866 |
|
546.07 |
1.46028 |
|
486.13 |
1.46333 |
|
479.99 |
1.46370 |
|
441.57 |
1.46642 |
|
435.835 |
1.46689 |
|
404.656 |
1.46982 |
|
365.015 |
1.47475 |
|
248.500 |
1.50849 |
|
193.300 |
1.56051 |
六、OHARA S-TIH53W熔融石英折射率表
|
入射光波长λ（nm） |
折射率 |
|
2325.42 |
1.78519 |
|
1970.09 |
1.79199 |
|
1529.58 |
1.80013 |
|
1128.64 |
1.80925 |
|
1013.98 |
1.81294 |
|
852.11 |
1.82021 |
|
768.19 |
1.82568 |
|
706.52 |
1.83098 |
|
656.27 |
1.83649 |
|
643.85 |
1.83807 |
|
632.8 |
1.83956 |
|
589.29 |
1.84635 |
|
587.56 |
1.84666 |
|
546.07 |
1.85504 |
|
486.13 |
1.87210 |
|
479.99 |
1.87431 |
|
441.57 |
1.89114 |
|
435.835 |
1.89419 |
|
404.656 |
1.91429 |
七、德国肖特BF33石英玻璃折射率表
|
波长（nm） |
折射率（n） |
|
248.3 |
1.525 |
|
296.7 |
1.504 |
|
365.0 |
1.489 |
|
435.8 |
1.480 |
|
480.0 |
1.477 |
|
546.1 |
1.473 |
|
587.6 |
1.471 |
|
632.8 |
1.470 |
|
643.8 |
1.470 |
|
852.1 |
1.465 |
|
1014.0 |
1.463 |
|
1529.6 |
1.456 |
八、德国肖特BK7石英玻璃折射率表
|
入射光波长λ（nm） |
折射率 |
|
2325.42 |
1.48921 |
|
1970.09 |
1.49495 |
|
1529.58 |
1.50091 |
|
1128.64 |
1.50669 |
|
1013.98 |
1.50731 |
|
852.11 |
1.50980 |
|
706.52 |
1.51289 |
|
656.27 |
1.51432 |
|
643.85 |
1.51472 |
|
632.8 |
1.51509 |
|
589.29 |
1.51673 |
|
587.56 |
1.51680 |
|
546.07 |
1.51872 |
|
486.13 |
1.52238 |
|
479.99 |
1.52283 |
|
435.835 |
1.52668 |
|
404.656 |
1.53024 |
|
365.000 |
1.53627 |
|
334.100 |
1.54272 |
|
312.600 |
1.54862 |
九、Heraeu Suprasil 3001/3002/300石英玻璃材料折射率表
|
入射光波长λ（nm） |
折射率 |
|
2325.42 |
1.4329 |
|
1970.00 |
1.4385 |
|
1529.58 |
1.4443 |
|
1064.00 |
1.4496 |
|
1013.98 |
1.4502 |
|
852.11 |
1.4525 |
|
706.52 |
1.4552 |
|
656.27 |
1.4564 |
|
643.85 |
1.4567 |
|
632.80 |
1.4570 |
|
589.29 |
1.4584 |
|
587.56 |
1.4585 |
|
546.07 |
1.4601 |
|
532.00 |
1.4607 |
|
486.13 |
1.4631 |
|
479.99 |
1.4635 |
|
435.83 |
1.4667 |
|
404.66 |
1.4696 |
|
365.01 |
1.4746 |
|
355.00 |
1.4761 |
|
334.15 |
1.4798 |
|
312.57 |
1.4845 |
|
296.73 |
1.4888 |
|
280.40 |
1.4941 |
|
248.40 |
1.5084 |
|
193.40 |
1.5602 |
十、Heraeu Infrasil 301/302石英玻璃材料折射率表
|
入射光波长λ（nm） |
折射率 |
|
2325.42 |
1.4331 |
|
1970.00 |
1.4387 |
|
1529.58 |
1.4442 |
|
1064.00 |
1.4497 |
|
1013.98 |
1.4503 |
|
852.11 |
1.4526 |
|
706.52 |
1.4553 |
|
656.27 |
1.4565 |
|
643.85 |
1.4568 |
|
632.80 |
1.4571 |
|
589.29 |
1.4585 |
|
587.56 |
1.4586 |
|
546.07 |
1.4602 |
|
532.00 |
1.4608 |
|
486.13 |
1.4632 |
|
479.99 |
1.4636 |
|
435.83 |
1.4668 |
|
404.66 |
1.4697 |
|
365.01 |
1.4747 |
|
355.00 |
1.4762 |
|
334.15 |
1.4799 |
|
312.57 |
1.4846 |
|
296.73 |
1.4889 |
|
280.40 |
1.4942 |
|
248.40 |
1.5085 |
|
193.40 |
1.5603 |
由光学熔融石英材料的波长-折射率的表中数据可知，相同波长下材料折射率从大到小的排序大致为：BF33 >（JGS1、JGS2、JGS3）≈SK-1300 > 7980。由于各厂商测试条件不同，此处无法准确计算同一波长下折射率的相差值，故只能将测试条件看似相同，粗略计算：
JGS1、JGS2、JGS3在波长为360nm时折射率为1.47529，波长为400nm时折射率为1.47012，将360nm-400nm波段折射率递减近似视为线性，即波长为365nm时JGS1折射率为1.47529-[（1.47529-1.47012）*5/40]=1.474643；康宁7980在波长为365nm时折射率为1.474539；SK-1300在20℃、波长为365nm时折射率为1.47459；肖特BF33在波长为365nm时折射率为1.489。因此在波长为365nm时，肖特BF33和JGS1、JGS2、JGS3折射率差值为1.4357 x 10-2；JGS1和SK-1300折射率差值为5.3 x 10-5；SK-1300和康宁7980折射率差值为5.1 x 10-5。
同理，在波长为435nm时JGS1、JGS2、JGS3折射率为1.466935，康宁7980折射率为1.466691，小原SK-1300折射率为1.46675，肖特BF33折射率为1.480。因此在波长为435nm时肖特BF33和JGS1折射率差值为1.3065 x 10-2，JGS1和SK-1300折射率差值为1.85 x 10-4，SK-1300和康宁7980折射率差值为5.9 x 10-5。
另外，在其他条件不变时，JGS1、JGS2、JGS3、康宁7980、SK-1300、肖特BF33、BK7等熔融石英镜片材料折射率均随波长的递增而减小，并且随着波长的逐渐增加，波长对熔融石英镜片折射率的影响逐渐减小。如果您需要熔融石英折射率的数据来源，请联系我们。